Influence of the second shell layer (TOPO, HDA) on the optical properties of CdSe/ZnS nanocrystal powder

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Zatryb, G. ; Podhorodecki, A. ; Misiewicz, J. ; Nauka, K.

Współtwórca:

Gaj, Miron. Redakcja

Temat i słowa kluczowe:

optyka ; nanocrystals ; photoluminescence ; CdSe/ZnS ; HDA ; TOPO

Opis:

Optica Applicata, Vol. 37, 2007, nr 4, s. 459-464

Abstrakt:

CdSe/ZnS nanocrystal powder covered with an additional cap layer (II-shell) of hexadecylamine (HDA) or tri-n-octylphosphine oxide (TOPO) has been investigated by using photoluminescence (PL) and total photoluminescence excitation (TPLE) spectroscopy. Depending on II-shell composition, different emission properties of the system have been observed. Strong emission bands at 2.00 eV and 1.95 eV related to nanocrystalline CdSe core recombination have been observed for TOPO and HDA-CdSe/ZnS nanocrystals, respectively. In both cases, weak emission bands centered at 3.5 and 2.8 eV have also been found. Moreover, in the case of TOPO II-shell, emission band at 1.65 eV related to defect state recombination has been observed. In both cases, similar absorption properties have been found, indicating that II-shell composition does not change nanocrystal absorption properties in an efficient way.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2007

Typ zasobu:

artykuł

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 37, 2007 ; Optica Applicata, Vol. 37, 2007, nr 4 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska