Struktura obiektu
Tytuł:

Borate glasses with PbO and PbCl2 containing Dy3+ ions

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Pisarska, Joanna

Współtwórca:

Gaj, Miron. Redakcja ; Urbańczyk, Wacław. Redakcja

Temat i słowa kluczowe:

optyka ; glasses ; dysprosium ions ; optical properties

Opis:

Optica Applicata, Vol. 40, 2010, nr 2, s. 367-374

Abstrakt:

Oxychloroborate glasses containing Dy3+ ions in the B2O3–PbCl2–PbO–Al2O3–WO3 system were studied using X-ray diffraction, Raman, FT-IR, absorption, excitation and luminescence spectroscopy. The results concerning glass preparation, short-range order structure and optical properties are reported. X-ray diffraction analysis evidently indicates that the fully amorphous system was prepared. Coexistence of trigonal BO3 and tetrahedral BO4 units was evidenced by Raman and FT-IR spectroscopy. The electronic states belonging to the 4f9 configuration of trivalent Dy3+ were determined from the absorption and excitation spectra. The luminescence bands at 480, 573 and 662 nm were registered in oxychloride glasses, which correspond to transitions originating from the 4F9/2 state to the 6HJ/2 (J = 11, 13, 15) states of Dy3+.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2010

Typ zasobu:

artykuł

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 40, 2010 ; Optica Applicata, Vol. 40, 2010, nr 2 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska

×

Cytowanie

Styl cytowania: