Influence of the composition of M78Si9B13 metallic glasses on their structural stability

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Jakubczyk, Ewa ; Stępień, Zdzisław ; Jakubczyk, Mieczysław

Współtwórca:

Gaj, Miron. Redakcja ; Wilk, Ireneusz. Redakcja

Temat i słowa kluczowe:

optyka ; metallic glasses ; crystallization ; Hall effect

Opis:

Optica Applicata, Vol. 35, 2005, nr 3, s. 339-346

Abstrakt:

The structural stability of Co78Si9B13 and Fe78Si9B13 metallic glasses was investigated by differential scanning calorimetry (DSC), X-ray diffraction, Hall effect and electrical resistivity methods. It was found that at first isochronal annealing leads to the formation of a-M (M = Co, Fe) phases.This process is followed by the formation of M2B phases. The phases were identified by X-ray diffraction method and their structures were confirmed with the use of quantum chemistry method. The creation of crystalline phases decreases abruptly the Hall and electrical resistivities. The alloy containing Fe appeared to have a much wider range of structural stability.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2005

Typ zasobu:

artykuł

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 35, 2005 ; Optica Applicata, Vol. 35, 2005, nr 3 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska

×

Cytowanie

Styl cytowania: