Effect of prefiring temperature on the texture and optical property of Bi4Ti3O12/MgO(100) prepared by using a metal naphthenate precursor

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Hwangbo, Seung ; Hwang, Kyu-Seog ; Kim, Jin-Tae

Współtwórca:

Gaj, Miron. Redakcja ; Urbańczyk, Wacław. Redakcja

Temat i słowa kluczowe:

optyka ; prefiring temperature ; metal naphthenate ; texture ; optical property

Opis:

Optica Applicata, Vol. 38, 2008, nr 4, s. 635-641

Abstrakt:

The effect of prefiring temperature on the crystal structure and optical property of the Bi4Ti3O12 films on MgO substrates by using a metal naphthenate precursor was investigated. As-deposited films were prefired at 300 °C, 400 °C and 500 °C for 10 min, followed by annealing at 750 °C for 30 min. According to the pole-figure analysis, texture of the annealed films was found to depend on prefiring temperature. Transmittance and the variation of band gap with prefiring temperature were studied.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2008

Typ zasobu:

artykuł

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 38, 2008 ; Optica Applicata, Vol. 38, 2008, nr 4 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska